Beilstein J. Org. Chem. 2010, 6, No. 51, doi:10.3762/bjoc.6.51
Graphical Abstract
Scheme 1: Hexapentyloxytriphenylene (HAT5).
Figure 1: Optical microscopy textures of a film prepared by drop-casting on heating to the isotropic phase an...
Figure 2: Optical microscopy images of a spin-coated sample with linear structures thick enough to be detecte...
Figure 3: AFM scan of a thick rope, of similar size to the linear structures observed by optical microscopy. ...
Figure 4: Thinner, isolated fibers, similar to the ones constituting the larger rope in Figure 3 are present in other...
Figure 5: Small, elongated aggregates form a nematic-like texture, possibly due to the formation of a lyonema...
Figure 6: AFM image of a spin-coated sample from a solution of 6 mg/ml. Below the surface profile along the w...
Figure 7: AFM image of the sample prepared from a concentration of 3 mg/ml.
Figure 8: Surface topography of the sample prepared from a concentration of 1.5 mg/ml visualized by AFM. The ...
Figure 9: Higher resolution scans of the fiber structure of the low concentration sample.
Beilstein J. Org. Chem. 2009, 5, No. 58, doi:10.3762/bjoc.5.58
Figure 1: Schematic illustration of the main parts of the setup used in our lab for coaxial electrospinning a...
Figure 2: Polarizing optical microscopy photographs of 8CB-containing composite fibres; (a) SmA phase at room...
Figure 3: Microscopy photographs of characteristic samples when varying the flow rate of the liquid crystal in...
Figure 4: Outer fibre diameters as a function of LC flow rate as determined from 50 measurements by optical m...
Figure 5: DSC thermograms on heating of 8CB as bulk and as inclusion compound in PVP fibres produced with dif...
Figure 6: The liquid crystal core shows a transformation from bubbly to smooth and to bubbly again with incre...
Figure 7: Influence of the applied voltage and the flow rate of the polymer solution on the mean fibre diamet...
Figure 8: a), b): 2D X-ray diffraction pattern of oriented fibres at two perpendicular roll-up directions sch...
Figure 9: X-ray diffraction patterns of PVP fibres without LC (a) and of surface-aligned samples of bulk 8CB ...
Figure 10: Schematic sketch of the arrangement of LC molecules and the smectic layers in an electrospun fibre.